Type: nail wire
Production method: electroplating, hot-dip galvanizing
1. Material: SAE1006, 1008, Q195, Q235, etc.
2. Wire diameter: 1.8-5.0 mm
3. Strength: 500-900MPA
4. Surface: Bright (zinc layer reaches 20-300g/m2)
5. Packaging: 100-1000KG/roll, inner plastic outer fiber
6. Purpose: Used for making nails in the construction and home decoration fields
The nail wire is produced strictly according to the quality standard to meet the customer's nail production requirements.
Type: breeding wire
Production method: hot-dip
1. Material: Q195, Q235, etc.
2. Wire diameter: 1.8-5.0 mm
3. Strength: 500-900MPA
4. Surface: Bright (zinc layer reaches 60-300g/m2)
5. Packaging: 500KG/roll, inner plastic outer fiber
6. Purpose: Used to make cages for raising chickens, pigeons, rabbits, etc.
Type: special wire for bucket handle
Production method: hot-dip galvanizing, electroplating
1. Material: Q195 coil
2. Wire diameter: 2.8-5.0 mm
3. Strength: 500-600MPA
4. Surface: bright (zinc layer reaches 20-50 g/m2)
5. Packaging: 500kg/roll, 800kg/roll, inner plastic outer fiber
6. Purpose: Used for making flower basket buckets, special silk for plastic bucket handles
Type: special wire for one-time hangers
Production method: hot-dip galvanizing, electroplating
1. Material: Q195, SAE1006, etc.
2. Wire diameter: 1.8-2.0 mm
3. Strength: 500-600MPA
4. Surface: bright (zinc layer reaches 20-50 g/m2)
5. Packaging: 500kg/roll, 800kg/roll, inner plastic outer fiber
6. Purpose: Used to make disposable hangers
Type: Galvanized steel wire for packaging
Manufacturing methods: heat plating, electroplating
1. Material: 55-75 # Steel plates
2. Line diameter: 1.8-3.8 mm
3. Strength: 900-1300 MPA
4. Surface: bright (zinc layer reaches 20-50 g / m 2)
5.Package: 500KG\ volume, 800KG\ volume, plastic inside and fiber outside
6. Use: For packaging of paper, cotton, hay, garbage and similar materials
Type: Wire for net-making products
Production method: hot-dip galvanizing, electroplating
1. Material: SAE1006, 1008, Q195, Q235, etc.
2. Wire diameter: 1.8-5.0 mm
3. Strength: 500-900MPA
4. Surface: bright (zinc layer reaches 20-50 g/m2)
5. Packaging: 500kg/roll, 800kg/roll, inner plastic outer fiber
6. Purpose: weaving, welding, weaving
Types: farming, stone cage net
Manufacturing method: 10% zinc aluminum alloy coated wire
1, material: Q195, Q235 and other wire rod
2. Line diameter: 1.8 - 5.0 mm
3. Strength: 500-900 MPA
4. Surface: bright (zinc layer reaches 200-300 g / m 2)
5.Package: 500KG\ volume, 800KG\ volume, plastic inside and fiber outside
6. Uses: breeding cages, stone cage nets, industrial products
It is composed of 10% Al-90% Zn alloying and a small amount of rare earth elements. Zn-Al alloy steel wire has a good corrosion resistance, the corrosion resistance of its products is about 5-10 times of ordinary pure galvanized steel wire. The corrosion resistance of the alloy zinc coated steel wire is superior to that of common zinc plating and electrolytic zinc plating whether in outdoor, humid or sea weather. The ductility and deformation ability of the alloy zinc layer steel wire is extremely strong, even beyond the steel substrate it protects. It can withstand the test of twisting and bending under the strong deformation process conditions without worrying about the cracking and falling of the zinc layer.
Type: Professional wire for environmental protection equipment accessories
Production method: hot-dip galvanizing, electroplating
1. Material: Q195, Q235, etc.
2. Wire diameter: 2.8-5.0 mm
3. Strength: 500-900MPA
4. Surface: bright (zinc layer reaches 20-50 g/m2)
5. Packaging: 100kg/roll, 500kg/roll, inner plastic outer fiber
6. Purpose: bag cage, mother-and-son frame,
Type: Special galvanized steel wire
Manufacturing method: Electroplating
1. Material: 45-72 # Steel
2. Line diameter: 1.6 - 2.0 mm
3. Strength: 800-1200 MPA
4. Surface: bright, matte (zinc layer reaches 40-50 g / m 2)
5.Package: 500KG\ volume, 800KG\ volume, plastic inside and fiber outside
6. Use: To be used as thin steel wire, brake wire, and other industrial wire
Type: Copper-plated steel wire
Production method: electroplating
1. Material: 45-72# steel
2. Wire diameter: 0.12-0.4 mm
3. Strength: 2100-3000MPA
4. Surface: Copper plating (zinc layer of 15-30 g/m2)
5. Packaging: BP50 25KG/axle, pallet carton packaging
6. Uses: steel fibers, rubber hoses, automotive parts, springs and other industrial products
Type: Zinc-coated small wire
Production method: electroplating, hot-dip galvanizing
1. Material: 45-72# steel, SAE1006, 1008, Q195, Q235, etc.
2. Wire diameter: 0.12-0.4 mm
3. Strength: 1000-3000MPA
4. Surface: bright (zinc layer of 15-60 g/m2)
5. Packaging: BP50 25KG/axle, pallet carton packaging
6. Uses: filter mesh, steel fiber, crafts, automotive accessories, springs and other industrial products
Type: Corrosion-resistant copper-coated wire
Production method: electroplating
1. Material: 45-72# steel
2. Wire diameter: 1.4-2.0 mm
3. Strength: 800-1000MPA
4. Surface: Copper plating (zinc layer of 40-60 g/m2)
5. Packaging: work wheel, scattering line
6. Purpose: re-drawing
Type: cold-drawn galvanized wire
Production method: electroplating
1. Material: Q195, Q235
2. Wire diameter: 1.8-5.0 mm
3. Strength: 500-800MPA
4. Surface: bright (zinc layer of 15-60 g/m2)
5. Packaging: 100kg per bundle, 500kg per bundle, inner plastic outer fiber
6. Uses: bucket handles, welded mesh, crafts, making nails, etc.
Type: annealed black wire
Production method: annealing
2. Material: Q195, Q235
2. Wire diameter: 1.8-5.0 mm
3. Strength: 340-400MPA
4. Surface: Black
5. Packaging: 100kg per bundle, 500kg per bundle, inner plastic outer fiber
6. Purpose: Crafts, industrial products
Type: annealed steel wire
Production method: water bath annealing
3. Material: 45-72# steel
2. Wire diameter: 1.8-5.0 mm
3. Strength: 800-1000MPA
4. Surface: Black
5. Packaging: 800kg per bundle, 500kg per bundle, inner plastic outer fiber
6. Purpose: Deep-processed industrial products